とは何ですか 2024 アルミニウム合金?
“2024 アルミニウム合金” refers to a specific type of aluminum alloy that is commonly used in various industries. It is known for its high strength-to-weight ratio and good machinability. The alloy primarily consists of aluminum, with copper as the primary alloying element and small amounts of other elements such as magnesium and manganese. 一般 2024 aluminum alloys include 2024 アルミシート, 2024 アルミホイル, そして 2024 アルミコイル.
Is 2024 aluminum alloy the hardest aluminum?
How hard is aluminum alloy 2024? 2024 aluminum alloy is often utilized in applications that require lightweight yet strong materials, such as aerospace components, aircraft structures, and high-stress parts. Its excellent fatigue resistance makes it suitable for use in structural applications. The alloy can be heat-treated to further enhance its strength.
Chemical composition of 2024 アルミニウム合金:
| 標準: JIS H4000-1999 | ||||||||
| 合金 | そして | 鉄 | 銅 | ん | マグネシウム | Cr | 亜鉛 | アル |
| 2024 | 0.5 | 0.5 | 3.8-4.9 | 0.3-1.0 | 1.2-1.8 | 0.10 | 0.25 | Remainder |
合金 2024 aluminum mechanical properties:
| 抗張力 | 400-470 MPa (58,000-68,000 psi) |
| 降伏強さ | 280-310 MPa (40,000-45,000 psi) |
| Elastic Modulus | 73 GPa (10.6 x 10^6 psi) |
| 伸長 | 10-20% |
| 密度 | 2.78 g/cm3 (0.1 ポンド/インチ3). |
| 硬度 | T3 temper 40-45 HRC. |
AL2024 alloy features and application range:
This is a high-strength hard aluminum that can be strengthened by heat treatment. It has medium plasticity in the quenched and just-quenched state. It has good spot welding. It has a tendency to form intergranular cracks when it is welded by gas. The alloy can be hardened after quenching and cold work. The machinability is good, but the machinability is low after annealing: the corrosion resistance is not high, and anodic oxidation treatment and painting methods are often used to improve its corrosion resistance.
It is mainly used to make various high-load parts and components (but not including stamping forgings), such as skeleton parts, skins, bulkheads, ribs, spars, rivets and other working parts below 150 °C on aircraft.
とは何ですか 2024 aluminum sheet ASTM?
ASTM B209 is the standard specification for aluminum and aluminum alloy sheet and plate. The ASTM standard for 2024 aluminum is ASTM B209-12, which is the standard specification for 2024 aluminum aluminum and aluminum alloy sheets and plates.
This ASTM standard covers general requirements for aluminum and aluminum alloy sheet materials. It includes requirements for chemical composition, mechanical properties, heat treatment, dimensional tolerances and other specifications for various aluminum alloys, including 2024.
2024 アルミシート
の 2024 aluminum plate is a typical hard aluminum alloy in the aluminum-copper-magnesium system. の 2024 aluminum plate has higher hardness and better overall performance. This alloy is produced in many countries and is the most widely used among duralumin. The characteristics of this alloy are: 高強度, certain heat resistance, and can be used as working parts below 150°C.
2024 aluminum plate density
2024 アルミニウム合金, density is 2.85 g/cm3.
Heat treatment of 2024 アルミニウム合金板
アルミニウム合金 2024 has good plasticity in the annealed and newly quenched states, and the heat treatment strengthening effect is significant, but the heat treatment process requires strict requirements. アルミ板 2024 has poor corrosion resistance and can be effectively protected by pure aluminum covering; it is prone to cracks during welding, but it can be welded or riveted through special technology.
2024 t3 aluminum sheet
2024-T3 aluminum plate is an excellent choice for most processing techniques. 2024 T3 is a high-strength, heat-treatable alloy that offers good corrosion resistance and a high strength-to-weight ratio. 2024 t3 aluminum plate is a lightweight material with a semi-smooth surface and dull finish that is often machined to end-user specifications in a variety of applications, including aircraft, 海洋, motorsports, gears, computer parts and other commercial grade parts .
アルミシート 2024 対 5252
Certainly, here’s a side-by-side comparison of 2024 アルミ板と 5052 aluminum sheet in tabular form:
| 財産 | 2024 アルミ板 | 5052 アルミシート |
|---|---|---|
| Alloy Composition | Al-Cu-Mn-Mg | Al-Mg |
| 強さ | High strength, especially in T6 temper | Moderate to high strength |
| Heat Treatability | Yes (T3, T4, T6, T8) | Not heat-treatable (H32, H34) |
| 耐食性 | Reasonable; often requires protective measures in corrosive environments | 優れた耐食性 |
| Typical Applications | Aerospace structural components, aircraft skins, high-strength applications | Sheet metal fabrication, boat hulls, automotive panels, kitchen equipment, architectural and construction applications |
| 成形性 | Moderate | Good |
| 抗張力 (Typical) | Varies depending on temper; can exceed 70,000 psi (T6) | 約 31,000 psi (H32), 36,000 psi (H34) |
| Typical Thickness Range (in inches) | Varied (commonly thicker) | Varied (commonly thinner) |
Please note that the specific properties, 厚さ, and applications can vary depending