General description of 3004 アルミニウム合金

とは何ですか 3004 アルミニウム合金?

3004 aluminum alloy is same as 3003 アルミニウム,both of them are alloys in the wrought aluminium-manganese alloys family (3000 or 3xxx series).

3004 aluminium alloy is similar to the 3003 合金, the main alloying addition is manganese, except for the addition of approximately 1% マグネシウム.

The alloy 3004 is commonly used in the production of beverage cans. It was developed to satisfy the need of thinner gauges in can-stock, and thereby to some extent replaced its predecessor 3003 アルミニウム合金 in the making of beverage cans.

3004 aluminum alloy coil

Cans can be made thinner due to the addition of 1% マグネシウム, which contributes in solid solution strengthening.

Chemical composition of 3004 アルミニウム

Chemical composition of 3004 アルミニウム

要素	アル	マグネシウム	そして	鉄	銅	亜鉛	ん	Remainder
3004	95.6 に 98.2%	0.8 に 1.3%	0.3% 最大	0.7% 最大	0.25% 最大	0.25% 最大	1.0 に 1.5%	0.15% 最大

Source：Wiki of 3004 アルミニウム合金

Material properties of 3004 アルミニウム

3004 aluminum is a widely used alloy with high strength, good formability, good workability, excellent corrosion resistance, and drawing characteristics. It is non-heat treatable and shares many of the same applications as 3003 アルミシート.

Cans Manufacture

Alternate of 3004 アルミニウム合金

• • ASTM B209
  • ASTM B221
  • ASTM B313
  • ASTM B547
  • ASTM B548
  • SAE J454
  • UNS A93004

Mechanical properties of 3004 アルミニウム

3004 aluminum alloy is a wrought alloy, mostly used for stamping or cold working, so excellent tensile strength, yield strength, fatigue strength and other properties are particularly important;
3004 aluminum has 15 tempering states, different tempering states correspond to different performances, the following are the corresponding performances in several typical tempering states;

気性	極限引張強さ	Ultimate Yield Strength	せん断強度	Fatigue Strength	%	ブリネル
3004-○	180 MPa / 26,000 psi	69 MPa / 10,000 psi	110 MPa / 16,000 psi	97 MPa / 14,000 psi	20-25	45
3004-H34	215 MPa / 31,000 psi	170 MPa / 25,000 psi	115 MPa / 17,000 psi	105 MPa / 15,000 psi	10-17	52
3004-H36	240 MPa / 35,000 psi	200 MPa / 25,000 psi	125 MPa / 18,000 psi	105 MPa / 15,000psi	9-12	63
3004-H36	260 MPa / 38,000 psi	230 MPa / 33,000 psi	140 MPa / 20,000 psi	110 MPa / 16,000 psi	5-9	70
3004-H38	285 MPa / 41,000 psi	250 MPa / 36,000 psi	145 MPa / 21,000 psi	110 MPa / 16,000 psi	4-6	77

Specification parameters of 3004 アルミニウム合金

Alloys	3004 アル
気性	○,H112,H12,H14,H16,H18,H19,H22,H24,H26,H28,H32,H34,H36,H38;
製品	3004 aluminm sheet/plate,3004 アルミコイル,3004 アルミストリップ,3004 アルミホイル,3004 アルミサークル;
被削性	アルミニウム 3004 alloy has good machinability in the hard temper.
Forming	アルミニウム 3004 alloy can be formed using conventional hot working or cold working methods.
溶接	の 3004 aluminum alloy can be welded with TIG or MIG welding techniques.
Heat treatment	アルミニウム 3004 alloy is an non-heat treatable alloy.
Forging	3004 aluminum alloy is forged at temperatures ranging from 372 to 510°C (700 to 950°F).
Hot Working	アルミニウム 3004 alloy is hot worked at 260 to 483°C (500 to 900°F).
Hardening	アルミニウム 3004 alloy can be annealed by cold working.
アプリケーション	3004 aluminum alloy was developed to satisfy the need for thinner gauges in can-stock,it is good for drawn and ironed rigid containers (beverage cans), chemical handling and storage equipment, sheet metal work, builders’ hardware, incandescent and fluorescent lamp bases. It is also used in similar applications to 3003 アルミニウム.

3004 aluminum sheet with sydney paper

Physical properties of 3004 アルミニウム合金

Aluminum alloy al 3004 融点：633°C（1170°F）;
Density of al 3004:2.6-2.8 g/cm3（0.0939- 0.101 lb/in3）;

Difference between 3003 そして 3004 アルミニウム

3004 aluminum alloy is very similar to 3003 アルミニウム, they both have excellent corrosion resistance, high strength-to-mass ratio, 等, but adding a small amount of magnesium to 3004 alloy aluminum improves the strength of the alloy.

3004 aluminum container foil

They are all important members of 3000 series AL-MN alloy and cannot be heat treated.
In terms of application, both 3003 そして 3004 aluminum are used in the packaging industry and in the manufacture of kitchen and cookware.

difference in chemical composition

要素	アル	マグネシウム	そして	鉄	銅	亜鉛	ん	Remainder
3004	95.6 – 98.2%	0.8 – 1.3%	0.3% 最大	0.7% 最大	0.25% 最大	0.25% 最大	1.0 に 1.5%	0.15% 最大
3003	96.8 – 99%	–	0.6% 最大	0.7% 最大	0.05 – 0.20%	0.1% 最大	1.0 に 1.5%	0.15% 最大

The alloy 3004 is commonly used in the making of beverage cans. It was developed to satisfy the need for thinner gauges in can-stock, and thereby to some extent replaced its predecessor 3003 alloy in the making of beverage cans. Can-stock can be made thinner due to the addition of 1% マグネシウム, which contributes in solid solution strengthening.

3004 alloy aluminum usages

3004 aluminum alloy is a widely used aluminum alloy material. Its application range is similar to that of 3003 アルミニウム合金. It is generally used in can manufacturing (beverage cans), cooking utensils and kitchenware manufacturing, indoor and outdoor decoration and other industries.

3004 aluminum for building	3004 缶用アルミニウム	3004 aluminum for cookware

3004 Alloy Aluminum Quality Supplier Near Me

Huawei Aluminum has 22 years of experience in the production and sales of aluminum products, providing high-quality 3004 aluminum sheets/coils/strips/foils/discs and other products;
We provide high-quality products at low prices, short lead times and perfect service systems;
Huawei Aluminum is a reliable supplier of aluminum products, please contact us if you need to order.