Estándar: GB/T3190-1996
●Chemical composition:
Silicio nu'bu̲: 0.35
Nt'eme hierro: 0.6
Cobre Cu: 0.10
Manganeso Mn: 0.05
Magnesio Mg: 0.05
Zinc Zn: 0.10
Vanadium V: 0.05
Aluminio 'na ar: 99.35
Other: 0.03
●Propiedades mecánicas:
Resistencia a la tracción σb (Mpa) )≥75
Límite elástico condicional σ0.2 (Mpa) )≥35
Hñeti: Ya propiedades mecánicas ar longitudinales ar tubería da mpat'i ambiente
●Main features and scope of application:
Industrial pure aluminum has the characteristics of high plasticity, Resistencia ar corrosión, good electrical conductivity and thermal conductivity, but low strength and impenetrable
Strengthened by heat treatment, Maquinabilidad deficiente, acceptable contact welding, soldadura gas. Make more use of its advantages to make some tools
Structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, electronic tube isolation nets, wires, cables
Protective cover, net, wire core and aircraft ventilation system parts and decorations; 1035 aluminum alloy is industrial pure aluminum,
Has high plasticity, Resistencia ar corrosión, Conductividad eléctrica ne conductividad térmica, but low strength, heat treatment can not strengthen the cut
Poor machinability; soldadura gas, Soldadura ya átomo ya hidrógeno ne ya soldadura ya contacto, not easy to braze; Hei ar soportar ndunthe ya presiones, ar procesamiento ne ar extensión,
doblamiento.
●Heat treatment process:
1) Recocido ngutha: la temperatura de calentamiento es de 350-410 °C; dependiendo de ar espesor efectivo ar hñei, the holding time is between 30-120min; Refrigeración nge ar ndähi wa ya dehe.
2) High-temperature annealing: heating temperature 350-500°C; Nu'bu̲ espesor ar producto terminado ge ar ≥6 mm, the holding time is 10-30min;
3) Low temperature annealing: temperatura de calentamiento 150-250°C; holding time 2-3h; Refrigeración nge ar ndähi wa ya dehe
Contesta