Standard: GB/T3190-1996
●Chemical composition:
Silikon Ja: 0.35
Järn Fe: 0.6
Koppar Cu: 0.10
Mangan Mn: 0.05
Magnesium Mg: 0.05
Zink Zn: 0.10
Vanadin V: 0.05
Aluminium Al: 99.35
Other: 0.03
●Mekaniska egenskaper:
Draghållfasthet σb (MPa) )≥75
Villkorlig sträckgräns σ0,2 (MPa) )≥35
Notera: Längsgående mekaniska egenskaper hos rör vid rumstemperatur
●Main features and scope of application:
Industrial pure aluminum has the characteristics of high plasticity, korrosionsbeständighet, good electrical conductivity and thermal conductivity, but low strength and impenetrable
Strengthened by heat treatment, dålig bearbetbarhet, acceptable contact welding, gassvetsning. Make more use of its advantages to make some tools
Structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, electronic tube isolation nets, wires, kablar
Protective cover, net, wire core and aircraft ventilation system parts and decorations; 1035 aluminum alloy is industrial pure aluminum,
Has high plasticity, korrosionsbeständighet, elektrisk ledningsförmåga och värmeledningsförmåga, but low strength, heat treatment can not strengthen the cut
Poor machinability; gassvetsning, väteatomsvetsning och kontaktsvetsning, inte lätt att löda; lätt att motstå olika tryckbearbetning och förlängning,
böjning.
●Heat treatment process:
1) Snabb glödgning: uppvärmningstemperaturen är 350-410°C; beroende på materialets effektiva tjocklek, the holding time is between 30-120min; luft- eller vattenkylning.
2) High-temperature annealing: heating temperature 350-500°C; när tjockleken på den färdiga produkten är ≥6 mm, the holding time is 10-30min;
3) Low temperature annealing: uppvärmningstemperatur 150-250°C; holding time 2-3h; luft- eller vattenkylning