General description of 3004 alliage d'aluminium

Qu'est-ce que 3004 alliage d'aluminium?

3004 aluminum alloy is same as 3003 aluminium,both of them are alloys in the wrought aluminium-manganese alloys family (3000 or 3xxx series).

3004 aluminium alloy is similar to the 3003 alliage, the main alloying addition is manganese, except for the addition of approximately 1% magnésium.

The alloy 3004 is commonly used in the production of beverage cans. Il a été développé pour satisfaire le besoin de calibres plus fins dans les boîtes de conserve., et a ainsi remplacé dans une certaine mesure son prédécesseur 3003 alliage d'aluminium in the making of beverage cans.

3004 bobine en alliage d'aluminium

Cans can be made thinner due to the addition of 1% magnésium, which contributes in solid solution strengthening.

Composition chimique de 3004 aluminium

Composition chimique de 3004 aluminium

Élément	Al	Mg	Et	Fe	Cu	Zn	Mn	Reste
3004	95.6 à 98.2%	0.8 à 1.3%	0.3% maximum	0.7% maximum	0.25% maximum	0.25% maximum	1.0 à 1.5%	0.15% maximum

Source：Wiki of 3004 alliage d'aluminium

Material properties of 3004 aluminium

3004 aluminum is a widely used alloy with high strength, bonne formabilité, good workability, excellente résistance à la corrosion, and drawing characteristics. It is non-heat treatable and shares many of the same applications as 3003 feuille d'aluminium.

Cans Manufacture

Alternate of 3004 alliage d'aluminium

• • ASTMB209
  • ASTMB221
  • ASTM B313
  • ASTMB547
  • ASTM B548
  • SAEJ454
  • UNS A93004

Propriétés mécaniques de 3004 aluminium

3004 aluminum alloy is a wrought alloy, mostly used for stamping or cold working, so excellent tensile strength, yield strength, fatigue strength and other properties are particularly important;
3004 aluminum has 15 tempering states, different tempering states correspond to different performances, the following are the corresponding performances in several typical tempering states;

Caractère	Résistance à la traction ultime	Ultimate Yield Strength	Résistance au cisaillement	Résistance à la fatigue	%	Brinell
3004-Ô	180 MPa / 26,000 psi	69 MPa / 10,000 psi	110 MPa / 16,000 psi	97 MPa / 14,000 psi	20-25	45
3004-H34	215 MPa / 31,000 psi	170 MPa / 25,000 psi	115 MPa / 17,000 psi	105 MPa / 15,000 psi	10-17	52
3004-H36	240 MPa / 35,000 psi	200 MPa / 25,000 psi	125 MPa / 18,000 psi	105 MPa / 15,000psi	9-12	63
3004-H36	260 MPa / 38,000 psi	230 MPa / 33,000 psi	140 MPa / 20,000 psi	110 MPa / 16,000 psi	5-9	70
3004-H38	285 MPa / 41,000 psi	250 MPa / 36,000 psi	145 MPa / 21,000 psi	110 MPa / 16,000 psi	4-6	77

Specification parameters of 3004 alliage d'aluminium

Alliages	3004 AL
Caractère	Ô,H112,H12,H14,H16,H18,H19,H22,H24,H26,H28,H32,H34,H36,H38;
Des produits	3004 aluminm sheet/plate,3004 bobine d'aluminium,3004 bande d'aluminium,3004 feuille d'aluminium,3004 cercle en aluminium;
Usinabilité	Aluminium 3004 alloy has good machinability in the hard temper.
Forming	Aluminium 3004 alloy can be formed using conventional hot working or cold working methods.
Soudage	Le 3004 aluminum alloy can be welded with TIG or MIG welding techniques.
Heat treatment	Aluminium 3004 alloy is an non-heat treatable alloy.
Forging	3004 aluminum alloy is forged at temperatures ranging from 372 to 510°C (700 to 950°F).
Hot Working	Aluminium 3004 alloy is hot worked at 260 to 483°C (500 to 900°F).
Hardening	Aluminium 3004 alloy can be annealed by cold working.
Applications	3004 aluminum alloy was developed to satisfy the need for thinner gauges in can-stock,it is good for drawn and ironed rigid containers (beverage cans), chemical handling and storage equipment, travail de tôlerie, builders’ hardware, incandescent and fluorescent lamp bases. It is also used in similar applications to 3003 aluminium.

3004 feuille d'aluminium avec du papier Sydney

Physical properties of 3004 alliage d'aluminium

Aluminum alloy al 3004 melting point：633°C（1170°F）;
Density of al 3004:2.6-2.8 g/cm3（0.0939- 0.101 lb/in3）;

Différence entre 3003 et 3004 aluminium

3004 aluminum alloy is very similar to 3003 aluminium, they both have excellent corrosion resistance, high strength-to-mass ratio, etc., but adding a small amount of magnesium to 3004 alloy aluminum improves the strength of the alloy.

3004 feuille de récipient en aluminium

They are all important members of 3000 series AL-MN alloy and cannot be heat treated.
In terms of application, les deux 3003 et 3004 aluminum are used in the packaging industry and in the manufacture of kitchen and cookware.

difference in chemical composition

Élément	Al	Mg	Et	Fe	Cu	Zn	Mn	Reste
3004	95.6 – 98.2%	0.8 – 1.3%	0.3% maximum	0.7% maximum	0.25% maximum	0.25% maximum	1.0 à 1.5%	0.15% maximum
3003	96.8 – 99%	–	0.6% maximum	0.7% maximum	0.05 – 0.20%	0.1% maximum	1.0 à 1.5%	0.15% maximum

The alloy 3004 is commonly used in the making of beverage cans. It was developed to satisfy the need for thinner gauges in can-stock, et a ainsi remplacé dans une certaine mesure son prédécesseur 3003 alliage dans la fabrication de canettes de boissons. Can-stock can be made thinner due to the addition of 1% magnésium, which contributes in solid solution strengthening.

3004 alloy aluminum usages

3004 aluminum alloy is a widely used aluminum alloy material. Its application range is similar to that of 3003 alliage d'aluminium. It is generally used in can manufacturing (beverage cans), cooking utensils and kitchenware manufacturing, indoor and outdoor decoration and other industries.

3004 aluminum for building	3004 en aluminium pour canettes	3004 aluminum for cookware

3004 Alloy Aluminum Quality Supplier Near Me

Huawei Aluminum has 22 years of experience in the production and sales of aluminum products, providing high-quality 3004 aluminum sheets/coils/strips/foils/discs and other products;
We provide high-quality products at low prices, short lead times and perfect service systems;
Huawei Aluminum is a reliable supplier of aluminum products, please contact us if you need to order.