What is a sheet of 3004 Aluminium?
3004 aluminum sheet is one of the more commonly used 3000 series aluminum sheets. It belongs to aluminum-manganese alloy. Lembaran aluminium 3004 has higher strength than 3003, excellent formability and good corrosion resistance. It is a common anti-rust aluminum sheet in aluminum alloys.
Lembaran aluminium 3004 chemical composition
| Aloi aluminium 3004 alloy composition table(%) | ||||||||
| Aloi | Si | Cu | Mg | Zn | Mn | Fe | Lain-lain | Al |
| 3004 | 0.30 | 0.25 | 0.8-1.3 | 0.25 | 1.0-1.5 | 0.7 | 0.05 | Kekal |
3004 aluminum plate material properties
As an AL-Mn alloy, 3004 is not high in strength (slightly higher than 1000 siri aluminium tulen industri) and cannot be strengthened by heat treatment. Its mechanical properties can be improved through cold working methods.
It has high plasticity in the annealed state, good plasticity in semi-cold work hardening, low plasticity in cold work hardening, rintangan kakisan yang baik, kebolehkimpalan yang baik, and poor machinability.
3004 aluminum material alloy specifications
| Aloi aluminium 3004 specifications | |
| Gred | 3000 siri |
| perangai | O,H12, H22, H32, H14, H24, H34, H16, H26, H18 |
| Ketebalan | 0.2-800mm |
| Lebar | 80-2800mm |
| Panjang | 500-18000mm |
| Saiz | 4×8, 4×10, 48×96, or customized. |
| Pembekal | Huawei Aluminium |
3004 aluminum sheet physical properties
Aloi aluminium 3004 has good mechanical and physical properties. The following are some key physical properties of 3004 Plat aluminium.
| Lembaran aluminium 3004 physical properties | |
| Ketumpatan | 2.73g/cm³ |
| Melting point | 644°C (1191°F) |
| Thermal conductivity | 157 W/(m·K) |
| Coefficient of Thermal Expansion (CTE) | 23.8 x 10^-6/°C |
| Specific heat capacity | 0.897 J/(g·℃) |
| Kerintangan | 0.057 ohm/cm |
| Magnetic | Non-magnetic |
3004 aluminum sheet temper mechanical properties
3004 H14 aluminum temper:
Kekuatan tegangan: 190 Mpa (27.6 ksi)
Kekuatan Hasil: 165 Mpa (24.0 ksi)
Pemanjangan: 10%
3004 H16 aluminum temper:
Kekuatan tegangan: 215 Mpa (31.2 ksi)
Kekuatan Hasil: 190 Mpa (27.6 ksi)
Pemanjangan: 5%
3004 H18 aluminum temper:
Kekuatan tegangan: 230 Mpa (33.4 ksi)
Kekuatan Hasil: 205 Mpa (29.7 ksi)
Pemanjangan: 4%
3004 H22 aluminum temper:
Kekuatan tegangan: 195 Mpa (28.3 ksi)
Kekuatan Hasil: 145 Mpa (21.0 ksi)
Pemanjangan: 8%
3004 H24 aluminum temper:
Kekuatan tegangan: 220 Mpa (31.9 ksi)
Kekuatan Hasil: 170 Mpa (24.7 ksi)
Pemanjangan: 6%
3004 H26 aluminum temper:
Kekuatan tegangan: 240 Mpa (34.8 ksi)
Kekuatan Hasil: 200 Mpa (29.0 ksi)
Pemanjangan: 4%
Kelebihan daripada 3004 kepingan aluminium
Aloi aluminium 3004 has many advantages and has many applications in multiple scenarios.
1. Rintangan kakisan: 3004 aluminum alloy has excellent corrosion resistance, which can prevent rust and degradation, and the corrosion resistance will be better after the surface is treated with coating.
2. Keupayaan borang: 3004 aluminum sheet has good formability and can be easily processed into various shapes without cracking or weakening. Can make beverage cans, car parts, and kitchen utensils.
3. Kekuatan yang lebih tinggi: 3004 aluminum sheet is weaker than other aluminum alloys such as 6061 atau 7075, tetapi 3004 aluminum plate has sufficient strength and can be used for lightweight structural components and panels.
4. Light weight and small weight: The density of aluminum plate is small, and the overall weight is much lighter. The low density of 3004 makes it an application where weight reduction is a priority, seperti industri automotif dan aeroangkasa.
5. Heat resistance: 3004 aluminum sheet has good heat resistance and maintains structural integrity at high temperatures without significant deformation or weakening.
These advantages make 3004 aluminum sheet a versatile material suitable for a wide range of applications, including automotive parts, food and beverage packaging, construction materials, kitchenware, dan banyak lagi.
3004 aluminum sheet product standard
Huawei Aluminum can be produced according to multiple standards.
ASTM B 209
ASTM B 221
ASTM B 547
ISO 6361
Rujukan：OpenAi
3000 lembaran aluminium siri
3105 kepingan aluminium
Tinggalkan pesanan