What is a sheet of 3004 aluminium?
3004 aluminum sheet is one of the more commonly used 3000 series aluminum sheets. It belongs to aluminum-manganese alloy. Arkusz aluminium 3004 has higher strength than 3003, excellent formability and good corrosion resistance. It is a common anti-rust aluminum sheet in aluminum alloys.
Arkusz aluminium 3004 chemical composition
| Aluminum alloy 3004 alloy composition table(%) | ||||||||
| Stop | I | Cu | Mg | Zn | Mn | Fe | Other | Glin |
| 3004 | 0.30 | 0.25 | 0.8-1.3 | 0.25 | 1.0-1.5 | 0.7 | 0.05 | Pozostać |
3004 aluminum plate material properties
As an AL-Mn alloy, 3004 is not high in strength (slightly higher than 1000 seria przemysłowa z czystego aluminium) and cannot be strengthened by heat treatment. Its mechanical properties can be improved through cold working methods.
It has high plasticity in the annealed state, good plasticity in semi-cold work hardening, low plasticity in cold work hardening, dobra odporność na korozję, good weldability, and poor machinability.
3004 aluminum material alloy specifications
| Stop aluminium 3004 specifications | |
| Stopień | 3000 seria |
| Hartować | O,H12, H22, H32, H14, H24, H34, H16, H26, H18 |
| Grubość | 0.2-800mm |
| Szerokość | 80-2800mm |
| Długość | 500-18000mm |
| Rozmiar | 4×8, 4×10, 48×96, or customized. |
| Dostawca | Aluminium Huawei |
3004 aluminum sheet physical properties
Aluminum alloy 3004 has good mechanical and physical properties. The following are some key physical properties of 3004 Aluminiowa płyta.
| Arkusz aluminium 3004 physical properties | |
| Gęstość | 2.73g/cm3 |
| Melting point | 644°C (1191°F) |
| Thermal conductivity | 157 W/(m·K) |
| Coefficient of Thermal Expansion (CTE) | 23.8 x 10^-6/°C |
| Specific heat capacity | 0.897 J/(g·℃) |
| Resistivity | 0.057 ohm/cm |
| Magnetic | Non-magnetic |
3004 aluminum sheet temper mechanical properties
3004 H14 aluminum temper:
Wytrzymałość na rozciąganie: 190 MPa (27.6 ksi)
Siła plonu: 165 MPa (24.0 ksi)
Wydłużenie: 10%
3004 H16 aluminum temper:
Wytrzymałość na rozciąganie: 215 MPa (31.2 ksi)
Siła plonu: 190 MPa (27.6 ksi)
Wydłużenie: 5%
3004 H18 aluminum temper:
Wytrzymałość na rozciąganie: 230 MPa (33.4 ksi)
Siła plonu: 205 MPa (29.7 ksi)
Wydłużenie: 4%
3004 H22 aluminum temper:
Wytrzymałość na rozciąganie: 195 MPa (28.3 ksi)
Siła plonu: 145 MPa (21.0 ksi)
Wydłużenie: 8%
3004 H24 aluminum temper:
Wytrzymałość na rozciąganie: 220 MPa (31.9 ksi)
Siła plonu: 170 MPa (24.7 ksi)
Wydłużenie: 6%
3004 H26 aluminum temper:
Wytrzymałość na rozciąganie: 240 MPa (34.8 ksi)
Siła plonu: 200 MPa (29.0 ksi)
Wydłużenie: 4%
Advantages of 3004 arkusz aluminium
Aluminum alloy 3004 has many advantages and has many applications in multiple scenarios.
1. Odporność na korozję: 3004 aluminum alloy has excellent corrosion resistance, which can prevent rust and degradation, and the corrosion resistance will be better after the surface is treated with coating.
2. Formability: 3004 aluminum sheet has good formability and can be easily processed into various shapes without cracking or weakening. Can make beverage cans, car parts, and kitchen utensils.
3. Higher strength: 3004 aluminum sheet is weaker than other aluminum alloys such as 6061 Lub 7075, but 3004 aluminum plate has sufficient strength and can be used for lightweight structural components and panels.
4. Light weight and small weight: The density of aluminum plate is small, and the overall weight is much lighter. The low density of 3004 makes it an application where weight reduction is a priority, such as the automotive and aerospace industries.
5. Heat resistance: 3004 aluminum sheet has good heat resistance and maintains structural integrity at high temperatures without significant deformation or weakening.
These advantages make 3004 aluminum sheet a versatile material suitable for a wide range of applications, including automotive parts, food and beverage packaging, construction materials, kitchenware, and more.
3004 aluminum sheet product standard
Huawei Aluminum can be produced according to multiple standards.
ASTM B 209
ASTM B 221
ASTM B 547
ISO 6361
Odniesienie：OpenAi