What is a sheet of 3004 alüminyum?
3004 aluminum sheet is one of the more commonly used 3000 series aluminum sheets. It belongs to aluminum-manganese alloy. Alüminyum levha 3004 göre daha yüksek bir güce sahiptir 3003, excellent formability and good corrosion resistance. It is a common anti-rust aluminum sheet in aluminum alloys.
Alüminyum levha 3004 kimyasal bileşim
| Alüminyum alaşım 3004 alloy composition table(%) | ||||||||
| Alaşım | Ve | cu | Mg | Zn | Mn | fe | Diğer | Al |
| 3004 | 0.30 | 0.25 | 0.8-1.3 | 0.25 | 1.0-1.5 | 0.7 | 0.05 | Geriye kalmak |
3004 aluminum plate material properties
As an AL-Mn alloy, 3004 is not high in strength (slightly higher than 1000 seri endüstriyel saf alüminyum) ısıl işlemle güçlendirilemez. Its mechanical properties can be improved through cold working methods.
It has high plasticity in the annealed state, good plasticity in semi-cold work hardening, low plasticity in cold work hardening, iyi korozyon direnci, iyi kaynaklanabilirlik, and poor machinability.
3004 aluminum material alloy specifications
| Alüminyum alaşımı 3004 specifications | |
| Seviye | 3000 seri |
| Öfke | Ö,H12, H22, H32, H14, H24, H34, H16, H26, H18 |
| Kalınlık | 0.2-800mm |
| Genişlik | 80-2800mm |
| Uzunluk | 500-18000mm |
| Boyut | 4×8, 4×10, 48×96, or customized. |
| Tedarikçi | Huawei Alüminyum |
3004 alüminyum levha fiziksel özellikleri
Alüminyum alaşım 3004 has good mechanical and physical properties. The following are some key physical properties of 3004 aliminyum tabak.
| Alüminyum levha 3004 fiziki ozellikleri | |
| Yoğunluk | 2.73g/cm³ |
| Erime noktası | 644°C (1191°F) |
| Termal iletkenlik | 157 W/(m·K) |
| Coefficient of Thermal Expansion (CTE) | 23.8 x 10^-6/°C |
| Özgül ısı kapasitesi | 0.897 J/(g·℃) |
| Direnç | 0.057 ohm/cm |
| Magnetic | Manyetik olmayan |
3004 aluminum sheet temper mechanical properties
3004 H14 aluminum temper:
Gerilme direnci: 190 MPa (27.6 ksi)
Akma dayanımı: 165 MPa (24.0 ksi)
Uzama: 10%
3004 H16 aluminum temper:
Gerilme direnci: 215 MPa (31.2 ksi)
Akma dayanımı: 190 MPa (27.6 ksi)
Uzama: 5%
3004 H18 aluminum temper:
Gerilme direnci: 230 MPa (33.4 ksi)
Akma dayanımı: 205 MPa (29.7 ksi)
Uzama: 4%
3004 H22 aluminum temper:
Gerilme direnci: 195 MPa (28.3 ksi)
Akma dayanımı: 145 MPa (21.0 ksi)
Uzama: 8%
3004 H24 aluminum temper:
Gerilme direnci: 220 MPa (31.9 ksi)
Akma dayanımı: 170 MPa (24.7 ksi)
Uzama: 6%
3004 H26 aluminum temper:
Gerilme direnci: 240 MPa (34.8 ksi)
Akma dayanımı: 200 MPa (29.0 ksi)
Uzama: 4%
Avantajları 3004 Alüminyum levha
Alüminyum alaşım 3004 has many advantages and has many applications in multiple scenarios.
1. korozyon direnci: 3004 aluminum alloy has excellent corrosion resistance, which can prevent rust and degradation, and the corrosion resistance will be better after the surface is treated with coating.
2. şekillendirilebilirlik: 3004 aluminum sheet has good formability and can be easily processed into various shapes without cracking or weakening. Can make beverage cans, car parts, and kitchen utensils.
3. Daha yüksek güç: 3004 aluminum sheet is weaker than other aluminum alloys such as 6061 veya 7075, Ancak 3004 aluminum plate has sufficient strength and can be used for lightweight structural components and panels.
4. Light weight and small weight: The density of aluminum plate is small, and the overall weight is much lighter. The low density of 3004 makes it an application where weight reduction is a priority, otomotiv ve havacılık endüstrileri gibi.
5. Heat resistance: 3004 aluminum sheet has good heat resistance and maintains structural integrity at high temperatures without significant deformation or weakening.
These advantages make 3004 aluminum sheet a versatile material suitable for a wide range of applications, including automotive parts, food and beverage packaging, inşaat malzemeleri, kitchenware, ve dahası.
3004 aluminum sheet product standard
Huawei Aluminum can be produced according to multiple standards.
ASTMB 209
ASTMB 221
ASTMB 547
ISO 6361
Referans：OpenAi