Ke eng 1060 Aluminium sheet grade?1060 aluminum plate is one of the 1000 lisebelisoa tsa aluminium, and the aluminum content of AL1060 is 99.6%. 1060 aluminum plate alloy is the most commonly used aluminum alloy in the 1XXX series, and the production speed of aluminum plate 1060 is fast, the production process is simple, the technology is relatively mature, and the price has a huge advantage compared with other series of aluminum alloys.
1060 letlapa la aluminium
1060 pure aluminium sheet
When the aluminum content of the aluminum plate reaches more than 99.6%, the 1060 aluminum plate is also called 1060 aluminium e hloekileng, 1060 aluminium e hloekileng haholo, le 1060 aluminium e hloekileng ea indasteri.
1060 aluminum alloy chemical composition standard:
| Standard: GB/T3190-1996 | |||||||||
| Alloy | Le | Fe | Cu | Mong | Mg | Zn | Ea | V | Al |
| 1060 | 0.25 | 035 | 0.05 | 0.03 | 0.03 | 0.05 | 0.03 | 0.05 | 99.6 |
Letlapa la aluminium 1060 alloy properties standard
| Khalefo | Ho thatafala (HB) | Matla a tšepe (Rm) | Kotulo Matla (Rp0.2) | Elongation (A50) | Likaroloana |
| 1060-O | <40 | 60-95 MPa | ≥35 MPa | ≥12% | Aluminium e hloekileng, without any treatment, has good formability and plasticity. |
| 1060-H12 | ≥35 | ≥80 MPa | ≥35 MPa | ≥12% | After cold working and partial softening, it has high strength and good formability. |
| 1060-H14 | ≥40 | ≥95 MPa | ≥45 MPa | ≥10% | After cold working and partial softening, it has high strength and good corrosion resistance. |
| 1060-H16 | ≥50 | ≥120 MPa | ≥70 MPa | ≥8% | After cold working and full softening, it has high strength and good formability. |
| 1060-H18 | ≥55 | ≥135 MPa | ≥105 MPa | ≥6% | After cold working and full softening, it has high strength and good corrosion resistance. |
| 1060-H24 | ≥40 | ≥95 MPa | ≥35 MPa | ≥12% | After partial annealing, it has higher strength and better formability. |
| 1060-H26 | ≥45 | ≥110 MPa | ≥55 MPa | ≥10% | After partial annealing, it has higher strength and better corrosion resistance. |
| 1060-H32 | ≥60 | ≥150 MPa | ≥110 MPa | ≥4% | After slight cold working and partial softening, it has high strength and good formability. |
| 1060-H111 | ≤30 | 60-95 MPa | ≥20 MPa | ≥25% | After slight cold working and partial softening, it has high strength and good processability. |
| 1060-H112 | ≤25 | ≥70 MPa | ≥50 MPa | ≥12% | slightly cold worked and fully softened, with high strength and good processability. |
1060 aluminum sheet density
1060 aluminum plate is a common aluminum alloy material with a density of about 2.7g/cm³. The mass of 1060 aluminum plate per cubic centimeter is about 2.7 dikgerama. Boima ba 1060 may vary slightly due to manufacturing processes.
1xxx series aluminum sheet
What is al 1060 material sheet? 1060 is one of the 1000 letoto, with an aluminum content purity of 99.6%. There are other types of aluminum plates in this series of alloys.
1050 letlapa la aluminium
1200 letlapa la aluminium
1235 letlapa la aluminium
1350 letlapa la aluminium
Na 1060 aluminum sheet pure aluminum sheet?
1060 aluminum plate is a high-purity aluminum plate. The aluminum content of 1060 reaches more than 99.6%, and the content of other elements is very low, eseng ho feta 0.4%. Ka hona, in terms of material composition, 1060 aluminum sheet can be regarded as a pure aluminum plate. Ka nako e tšoanang, the high purity and good performance of aluminum sheet 1060 also make it widely used in various fields.
Casting process of 1060 letlapa la aluminium
The manufacturing process of 1060 aluminum sheet is continuous casting and rolling. This process can ensure the uniformity and purity of the aluminum plate, thus making the purity of the 1060 aluminum sheet higher. It can be better applied in light industry, electronic components, likarolo tsa koloi, building decoration and other fields.