6061-T6 and 7075 are both popular aluminum alloys, and while they share some similarities, there are also significant differences, particularly in strength, độ cứng, and applications. Here’s a brief comparison:

1.Strength comparison between 6061-T6 and 7075:

6061-T6 Aluminum Sheet Alloy: Has good strength and is often used in structural applications. But compared to 7075, overall it is not that strong.7075：Aluminum sheetAlloy 7075 is known for its high strength, making it suitable for applications where strength is a key factor.

2.Nhôm 6061 nhôm t6 vs 7075 độ cứng:

6061-T6 is less hard than 7075, which may be an advantage in some applications where machinability and formability are more important than maximum strength. 7075 aluminum plate has higher hardness because it contains zinc as an alloying element. This makes processing more challenging but provides greater strength.

tấm nhôm 6061 vs 7075

3.6061 t6 nhôm vs 7075 aluminum machinability comparison:

6061-T6 aluminum plates are generally easier to process and form, and are well suited for the production of complex shapes. 7075 aluminum plate is more difficult to process than 6061 due to its higher hardness.

4.6061-nhôm t6 vs 7075 chống ăn mòn:

Aluminum sheet Both alloys 6061 Và 7075 have good corrosion resistance, Nhưng 6061 may have a slight advantage in some environments due to the absence of zinc, which may be the source of galvanic corrosion in 7075.

5.Application comparison of aluminum plate 6061 t6 and 7075:

6061-T6 aluminum plates are commonly used in structural parts, bicycle frames, aerospace accessories, ship parts, and general mechanical parts.7075 aluminum sheet is widely used in aerospace applications, highly stressed structural components, and parts requiring high strength and low weight.

6.Nhôm 6061 vs 7075 Ingredients:

The main components of 6061 series aluminum alloy are magnesium and silicon, with zinc accounting for a very low proportion. The zinc component of the 7075 series aluminum alloy accounts for a relatively large proportion, reaching 6%. Ngoài ra, 7075 aluminum plate has a slightly higher magnesium content and also adds more copper to its chemical composition.

7.6061-nhôm t6 vs 7075 giá :

Because 7075 aluminum alloy has high strength and zinc content, its price is relatively high. Các 6061 aluminum alloy is relatively economical and affordable.

8.Nhôm 7075 vs 6061 practicality:

Since 7075 aluminum alloy contains a high proportion of other metals and is difficult to weld, it is generally not used as frame material. Since 6061 aluminum alloy contains a low proportion of other metals, it can be processed in various ways to increase its strength and reduce wind resistance. It can even be piped three times to reduce weight. Vì thế, 6061 aluminum alloy has good practicality.

9.Comparison of density between 6061 tấm nhôm và 7075 tấm nhôm

There is a difference in density between 6061 aluminum alloy and 7075 hợp kim nhôm. 6061 aluminum alloy is a common aluminum alloy, chủ yếu bao gồm nhôm, magnesium and silicon, with a density of approximately 2.70g/cm³ or (2700kg/m³). Các 7075 aluminum alloy is a high-strength aluminum alloy, chủ yếu bao gồm nhôm, kẽm, đồng, magnesium and other elements. Its density is approximately 2.81g/cm³ or (2810kg/m³). Vì thế, from a density perspective, the density of 7075 aluminum alloy is slightly higher than that of 6061 hợp kim nhôm.

10.Comparison of melting points between 6061 Và 7075 tấm nhôm

The melting points of 6061 aluminum alloy and 7075 aluminum alloy are the same, both around 660°C.

Tóm tắt, the choice between 6061-T6 and 7075 depends on the specific requirements of the application. If high strength and hardness are critical and machinability is not a major consideration, 7075 may be the first choice. If machinability, formability and strength balance are important, then 6061-T6 may be more suitable.